表一
|
序号 |
中国 |
日本 |
美国 |
英国 |
德国 |
法国 |
|
1 |
1Cr18Mn8Ni5N |
SUS202 |
202,S20200 |
284S16 |
X12CrNi177 |
Z12CN17.07 |
|
2 |
1Cr17Ni7 |
SUS301 |
301,S30100 |
301S21 |
X12CrNi188 |
Z10CN18.09 |
|
3 |
1Cr18Ni9 |
SUS302 |
302,S30200 |
302S25 |
X5CrNi189 |
Z6CN18.09 |
|
4 |
0Cr18Ni9 |
SUS304 |
304,S30300 |
304S15 |
X2CrNi189 |
Z2CN18.09 |
|
5 |
00Cr19Ni10 |
SUS304L |
304L,S30403 |
304S12 |
|
Z5CN18.09A2 |
|
6 |
0Cr19Ni9N |
SUS304N1 |
|
304N |
X2CrNiN1810 |
Z2CN18.10N |
|
7 |
00Cr18Ni10N |
SUS304LN |
|
|
X5CrNi1911 |
Z8CN18.12 |
|
8 |
1Cr18Ni12 |
SUS305 |
305,S30500 |
305S19 |
|
|
|
9 |
0Cr23Ni13 |
SUS309S |
309S,S30908 |
|
|
|
|
10 |
0Cr25Ni20 |
SUS310S |
310S,S31008 |
|
X5CrNiMo1812 |
Z6CND17.12 |
|
11 |
0Cr17Ni12Mo2 |
SUS316 |
316,S3160 |
316S16 |
X2CrNiMo1812 |
Z2CND17.12 |
|
12 |
00Cr17Ni14Mo2 |
SUS316L |
316L,S31603 |
316S12 |
|
|
|
13 |
0Cr17Ni12Mo2N |
SUS316N |
316N,S31651 |
|
|
|
|
14 |
00Cr18Ni14Mo2Cu2 |
SUS316JlL |
|
|
|
|
|
15 |
0Cr19Ni13Mo3 |
SUS317 |
317,S31700 |
317S16 |
X2CrNiMo1816 |
Z2CN19.15 |
|
16 |
00Cr19Ni13Mo3 |
SUS317L |
317L,S31703 |
317S12 |
X10CrNiTi189 |
|
|
17 |
1Cr18Ni9Ti |
|
|
|
|
|
|
18 |
0Cr19Ni10Ti |
SUS321 |
321,S32100 |
321S12 321S20 |
X10CrTi189 |
Z6NT18.10 |
|
19 |
0Cr18Ni11Nb |
SUS347 |
347,S34700 |
347S17 |
X10CrNiNb189 |
Z6NNb18.10 |
|
20 |
0Cr13Al |
SUS405 |
405,S40500 |
405S17 |
X71CrAl13 |
Z6CA13 |
|
21 |
1Cr17 |
SUS430 |
430,S43000 |
430S15 |
X8Cr17 |
Z8C17 |
|
22 |
00Cr27Mo |
SUSXM27 |
XM27,S44625 |
|
|
Z01CD26.1 |
|
23 |
1Cr12 |
SUS403 |
403,S40300 |
403S17 |
|
|
|
24 |
1Cr13 |
SUS410 |
410,S41000 |
410S21 |
X10Cr13 |
Z12C13 |
|
25 |
0Cr13 |
SUS410S |
410S |
403S17 |
X7Cr13 |
Z6C13 |
|
26 |
1Cr13Mo |
SUS410J1 |
|
|
|
|
|
27 |
2Cr13 |
SUS420J1 |
420,S42000 |
420S37 |
X20Cr13 |
Z20C13 |
|
28 |
3Cr13 |
SUS420J2 |
|
420S45 |
|
Z15CN16.02 |
|
29 |
1Cr17Ni2 |
SUS431 |
431,S43100 |
431S29 |
X22CrNi17 |
|
|
30 |
7Cr17 |
SUS440A |
440,S44002 |
|
|
|
|
31 |
8Cr17 |
SUS440B |
440,S44003 |
|
|
Z100CD17 |
|
32 |
9Cr18 |
SUS440C |
440C |
|
X105CrMo17 |
Z6CNU17.04 |
表二
|
No |
中国GB |
日本
JIS |
美国 |
韩国
KS |
欧盟BS EN |
印度
IS |
澳大利亚AS |
中国台湾
CNS |
||||
|
|
旧牌号 |
新牌号（07.10） |
|
ASTM |
UNS |
|
|
|
|
|
||
|
奥氏体不锈钢 |
||||||||||||
|
1 |
1Cr17Mn6Ni5N |
12Cr17Mn6Ni5N |
SUS201 |
201 |
S20100 |
STS201 |
1.4372 |
10Cr17Mn6Ni4N20 |
201-2 |
201 |
||
|
2 |
1Cr18Mn8Ni5N |
12Cr18Mn9Ni5N |
SUS202 |
202 |
S20200 |
STS202 |
1.4373 |
|
- |
202 |
||
|
3 |
1Cr17Ni7 |
12Cr17Ni7 |
SUS301 |
301 |
S30100 |
STS301 |
1.4319 |
10Cr17Ni7 |
301 |
301 |
||
|
4 |
0Cr18Ni9 |
06Cr19Ni10 |
SUS304 |
304 |
S30400 |
STS304 |
1.4301 |
07Cr18Ni9 |
304 |
304 |
||
|
5 |
00Cr19Ni10 |
022Cr19Ni10 |
SUS304L |
304L |
S30403 |
STS304L |
1.4306 |
02Cr18Ni11 |
304L |
304L |
||
|
6 |
0Cr19Ni9N |
06Cr19Ni10N |
SUS304N1 |
304N |
S30451 |
STS304N1 |
1.4315 |
- |
304N1 |
304N1 |
||
|
7 |
0Cr19Ni10NbN |
06Cr19Ni9NbN |
SUS304N2 |
XM21 |
S30452 |
STS304N2 |
- |
- |
304N2 |
304N2 |
||
|
8 |
00Cr18Ni10N |
022Cr19Ni10N |
SUS304LN |
304LN |
S30453 |
STS304LN |
- |
- |
304LN |
304LN |
||
|
9 |
1Cr18Ni12 |
10Cr18Ni12 |
SUS305 |
305 |
S30500 |
STS305 |
1.4303 |
- |
305 |
305 |
||
|
10 |
0Cr23Ni13 |
06Cr23Ni13 |
SUS309S |
309S |
S30908 |
STS309S |
1.4833 |
- |
309S |
309S |
||
|
11 |
0Cr25Ni20 |
06Cr25Ni20 |
SUS310S |
310S |
S31008 |
STS310S |
1.4845 |
- |
310S |
310S |
||
|
12 |
0Cr17Ni12Mo2 |
06Cr17Ni12Mo2 |
SUS316 |
316 |
S31600 |
STS316 |
1.4401 |
04Cr17Ni12Mo2 |
316 |
316 |
||
|
13 |
0Cr18Ni12Mo3Ti |
06Cr17Ni12Mo2Ti |
SUS316Ti |
316Ti |
S31635 |
- |
1.4571 |
04Cr17Ni12MoTi20 |
316Ti |
316Ti |
||
|
14 |
00Cr17Ni14Mo2 |
022Cr17Ni12Mo2 |
SUS316L |
316L |
S31603 |
STS316L |
1.4404 |
~02Cr17Ni12Mo2 |
316L |
316L |
||
|
15 |
0Cr17Ni12Mo2N |
06Cr17Ni12Mo2N |
SUS316N |
316N |
S31651 |
STS316N |
- |
- |
316N |
316N |
||
|
16 |
00Cr17Ni13Mo2N |
022Cr17Ni13Mo2N |
SUS316LN |
316LN |
S31653 |
STS316LN |
1.4429 |
- |
316LN |
316LN |
||
|
17 |
0Cr18Ni12Mo2Cu2 |
06Cr18Ni12Mo2Cu2 |
SUS316J1 |
- |
- |
STS316J1 |
- |
- |
316J1 |
316J1 |
||
|
18 |
00Cr18Ni14Mo2Cu2 |
022Cr18Ni14Mo2Cu2 |
SUS316J1L |
- |
- |
STS316J1L |
- |
- |
- |
316J1L |
||
|
19 |
0Cr19Ni13Mo3 |
06Cr19Ni13Mo3 |
SUS317 |
317 |
S31700 |
STS317 |
- |
- |
317 |
317 |
||
|
20 |
00Cr19Ni13Mo3 |
022Cr19Ni13Mo3 |
SUS317L |
317L |
S31703 |
STS317L |
1.4438 |
- |
317L |
317L |
||
|
21 |
0Cr18Ni10Ti |
06Cr18Ni11Ti |
SUS321 |
321 |
S32100 |
STS321 |
1.4541 |
04Cr18Ni10Ti20 |
321 |
321 |
||
|
22 |
0Cr18Ni11Nb |
06Cr18Ni11Nb |
SUS347 |
347 |
S34700 |
STS347 |
1.4550 |
04Cr18Ni10Nb40 |
347 |
347 |
||
|
奥氏体-铁素体型不锈钢（双相不锈钢） |
||||||||||||
|
23 |
0Cr26Ni5Mo2 |
- |
SUS329J1 |
329 |
S32900 |
STS329J1 |
1.4477 |
- |
329J1 |
329J1 |
||
|
24 |
00Cr18Ni5Mo3Si2 |
022Cr19Ni5Mo3Si2N |
SUS329J3L |
- |
S31803 |
STS329J3L |
1.4462 |
- |
329J3L |
329J3L |
||
|
铁素体型不锈钢 |
||||||||||||
|
25 |
0Crl3Al |
06Crl3Al |
SUS405 |
405 |
S40500 |
STS405 |
1.4002 |
04Cr13 |
405 |
405 |
||
|
26 |
- |
022Cr11Ti |
SUH409 |
409 |
S40900 |
STS409 |
1.4512 |
- |
409L |
409L |
||
|
27 |
00Cr12 |
022Cr12 |
SUS410L |
- |
- |
STS410L |
- |
- |
410L |
410L |
||
|
28 |
1Cr17 |
10Cr17 |
SUS430 |
430 |
S43000 |
STS430 |
1.4016 |
05Cr17 |
430 |
430 |
||
|
29 |
1Cr17Mo |
10Cr17Mo |
SUS434 |
434 |
S43400 |
STS434 |
1.4113 |
- |
434 |
434 |
||
|
30 |
- |
022Cr18NbTi |
- |
- |
S43940 |
- |
1.4509 |
- |
439 |
439 |
||
|
31 |
00Cr18Mo2 |
019Cr19Mo2NbTi |
SUS444 |
444 |
S44400 |
STS444 |
1.4521 |
- |
444 |
444 |
||
|
马氏体型不锈钢 |
||||||||||||
|
32 |
1Cr12 |
12Cr12 |
SUS403 |
403 |
S40300 |
STS403 |
- |
- |
403 |
403 |
||
|
33 |
1Cr13 |
12Cr13 |
SUS410 |
410 |
S41000 |
STS410 |
1.4006 |
12Cr13 |
410 |
410 |
||
|
34 |
2Cr13 |
20Cr13 |
SUS420J1 |
420 |
S42000 |
STS420J1 |
1.4021 |
20Cr13 |
420 |
420J1 |
||
|
35 |
3Cr13 |
30Cr13 |
SUS420J2 |
- |
- |
STS420J2 |
1.4028 |
30 Cr13 |
420J2 |
420J2 |
||
|
36 |
7Cr17 |
68Cr17 |
SUS440A |
440A |
S44002 |
STS440A |
- |
- |
440A |
440A |
||
奥氏体不锈钢
奥氏体不锈钢：在常温下具有奥氏体组织的不锈钢。钢中含Cr约18%、Ni 8%~10%、C约0.1%时，具有稳定的奥氏体组织。奥氏体铬镍不锈钢包括著名的18Cr-8Ni钢和在此基础上增加Cr、Ni含量并加入Mo、Cu、Si、Nb、Ti等元素发展起来的高Cr-Ni系列钢。奥氏体不锈钢无磁性而且具有高韧性和塑性，但强度较低，不可能通过相变使之强化，仅能通过冷加工进行强化。如加入S，Ca，Se，Te等元素，则具有良好的易切削性。此类钢除耐氧化性酸介质腐蚀外，如果含有Mo、Cu等元素还能耐硫酸、磷酸以及甲酸、醋酸、尿素等的腐蚀。此类钢中的含碳量若低于0.03%或含Ti、Ni，就可显著提高其耐晶间腐蚀性能。高硅的奥氏体不锈钢浓硝酸肯有良好的耐蚀性。由于奥氏体不锈钢具有全面的和良好的综合性能，在各行各业中获得了广泛的应用。
奥氏体型钢
(1)1Cr17Mn6Ni15N；(2)1Cr18Mn8Ni5N；(3)1Cr18Ni9；(4)1Cr18Ni9Si3；(5)0Cr18Ni9；(6)00Cr19Ni10；(7)0Cr19Ni9N；(8)0Cr19Ni10NbN；(9)00Cr18Ni10N；(10)1Cr18Ni12；(11) 0Cr23Ni13；(12)0Cr25Ni20；(13) 0Cr17Ni12Mo2；(14) 00Cr17Ni14Mo2；(15) 0Cr17Ni12Mo2N；(16) 00Cr17Ni13Mo2N；(17) 1Cr18Ni12Mo2Ti；(18) 0Cr18Ni12Mo2Ti；(19) 1Cr18Ni12Mo3Ti；(20) 0Cr18Ni12Mo3Ti；(21) 0Cr18Ni12Mo2Cu2；(22) 00Cr18Ni14Mo2Cu2；(23) 0Cr19Ni13Mo3；(24) 00Cr19Ni13Mo3；(25) 0Cr18Ni16Mo5；(26) 1Cr18Ni9Ti；(27) 0Cr18Ni10Ti；(28) 0Cr18Ni11Nb；(29) 0Cr18Ni13Si4
1.概述
奥氏体不锈钢1913年在德国问世，在不锈钢中一直扮演着最重要的角色，其生产量和使用量约占不锈钢总产量及用量的70%。钢号也最多，当今我国常用奥氏体不锈钢的牌号就有40多个，最常见的就是18-8型。
定义：常温下具有奥氏体组织的不锈钢。
分类：Fe-Cr-Ni (主体)
Fe-Cr-Mn
国内外牌号对比：
GB(中国) ASTM(美国) JIS(日本) DIN(德国)
1Cr17Ni7 301 SUS301 X12CrNi177
1Cr18Ni9 302 SUS302 X12CrNi188
1Cr18Ni10 303 SUS303 X12CrNiS188
0Cr18Ni9 304 SUS304 X5CrNi189
0Cr19i10 304L SUS304L X2CrNi189
0Cr17Ni12Mo2 316 SUS316 X5CrNiMo1810
00Cr17Ni14Mo2 316L SUS316L X2CrNiMo1810
0Cr18Ni10Ti 321 SUS321 X10CrNiTi189
0Cr19Ni13Mo3 317 SUS317 X2CrNiMo1816
2. 奥氏体不锈钢的成分
在18-8型不锈钢的成分基础上演变，主要有以下几方面的重要发展：
1) 加Mo改善点蚀和耐缝隙腐蚀
2) 降C或加Ti、Nb，减少晶间腐蚀倾向
3) 加Ni和Cr改善高温抗氧化性和强度
4) 加Ni改善抗应力腐蚀性能.转自"我要不锈钢"
5) 加S、Se改善切削性和构件表面精度.
奥氏体不锈钢成分系统图
3. 奥氏体不锈钢的组织
3.1铁素体相的形成
3.1.1铁素体相对奥氏体不锈钢性能的影响
F相的出现一般都对奥氏体不锈钢的性能带来不利的影响：如使热加工产生裂纹的倾向性增大；钢的耐点蚀性下降，在诸多腐蚀环境（如尿素生产）中耐蚀性劣化；在高温下加长时间加热时，F相会转变为σ相使钢变脆等等。
3.1.2铁素体相的形成与含量的粗略判定
含量的粗略判定：
Creq=%Cr+1.5×%Si+%Mo，Nieq=%Ni+30×(%C+%N)+0.5×%Mn
3.1.3铁素体相的消除
根本的办法是提高钢中奥氏体形成元素的含量。Ni是首选的元素，但是从经济的角度出发，Mn和N也受到人们的重视。特别是N，其抑制铁素体形成的能, 力为Ni的30倍，同时又有改善耐蚀性和提高强度的作用.
马氏体不锈钢
标准的马氏体不锈钢是：403、410、414、416、416(Se)、420、431、440A、440B和440C型，这些钢材的耐腐蚀性来自“铬”，其范围是从11.5至18%，铬含量愈高的钢材需碳含量愈高，以确保在热处理期间马氏体的形成，上述三种440型不锈钢很少被考虑做为需要焊接的应用，且440型成份的熔填金属不易取得。
标准马氏体钢材的改良，含有类如镍、钼、钒等的添加元素，主要是用于将标准钢材受限的容许工作温度提升至高于1100K，当添加这些元素时，碳含量也增加，随着碳含量的增加，在焊接物的硬化热影响区中避免龟裂的问题变成更严重。
马氏体不锈钢能在退火、硬化和硬化与回火的状态下焊接，无论钢材的原先状态如何，经过焊接后都会在邻近焊道处产生一硬化的马氏体区，热影响区的硬度主要是取决于母材金属的碳含量，当硬度增加时，则韧性减少，且此区域变成较易产生龟裂、预热和控制层间温度，是避免龟裂的最有效方法，为得最佳的性质，需焊后热处理。
马氏体不锈钢是一类可以通过热处理（淬火、回火）对其性能进行调整的不锈钢，通俗地讲，是一类可硬化的不锈钢。这种特性决定了这类钢必须具备两个基本条件：一是在平衡相图中必须有奥氏体相区存在，在该区域温度范围内进行长时间加热，使碳化物固溶到钢中之后，进行淬火形成马氏体，也就是化学成分必须控制在γ或γ+α相区，二是要使合金形成耐腐蚀和氧化的钝化膜，铬含量必须在10.5%以上。按合金元素的差别，可分为马氏体铬不锈钢和马氏体铬镍不锈钢。
马氏体铬不锈钢的主要合金元素是铁、铬和碳。图1-4是Fe-Cr系相图富铁部分，如Cr大于13%时，不存在γ相，此类合金为单相铁素体合金，在任何热处理制度下也不能产生马氏体，为此必须在内Fe-Cr二元合金中加入奥氏体形成元素，以扩大γ相区，对于马氏体铬不锈钢来说，C、N是有效元素，C、N元素添加使得合金允许更高的铬含量。在马氏体铬不锈钢中，除铬外，C是另一个最重要的必备元素，事实上，马氏体铬不锈耐热钢是一类铁、铬、碳三元合金。当然，还有其他元素，利用这些元素，可根据Schaeffler图确定大致的组织。
马氏体不锈钢主要为铬含量在12%-18%范围内的低碳或高碳钢。各国广泛应用的马氏体不锈钢钢种有如下3类：
1.低碳及中碳13%Cr钢
2.高碳的18%Cr钢
3.低碳含镍（约2%）的17%Cr钢
马氏体不锈钢具备高强度和耐蚀性，可以用来制造机器零件如蒸汽涡轮的叶片（1Cr13）、蒸汽装备的轴和拉杆（2Cr13），以及在腐蚀介质中工作的零件如活门、螺栓等（4Cr13）。碳含量较高的钢号（4Cr13、9Cr18）则适用于制造医疗器械、餐刀、测量用具、弹簧等。
与铁素体不锈钢相似，在马氏体不锈钢中也可以加入其它合金元素来改进其他性能：1.加入0.07%S或Se改善切削加工性能，例如1Cr13S或4Cr13Se；2.加入约1%Mo及0.1% V，可以增加9Cr18钢的耐磨性及耐蚀性；3.加入约1Mo-1W-0.2V，可以提高1Cr13及2Cr13钢的热强性。
马氏体不锈钢与调制钢一样，可以使用淬火、回火及退火处理。其力学性质与调制钢也相似：当硬度升高时，抗拉强度及屈服强度升高，而伸长率、截面收缩率及冲击功则随着降低。
马氏体不锈钢的耐蚀性主要取决于铬含量，而钢中的碳由于与铬形成稳定的碳化铬，又间接的影响了钢的耐蚀性。因此在13%Cr钢中，碳含量越低，则耐蚀性越高。而在1Cr13、2Cr13、3Cr13及4Cr13四种钢中，其耐蚀性与强度的顺序恰好相反。